The PolyCore ASA-3012 pellets by Polymaker are made of ASA reinforced with 20 % of glass fibre. These pellets were developed specially for BAAM (Big Area Additive Manufacturing).
The PolyCore ASA-3012 pellets are characterized by excellent printability, low warping, great colorability and strong mechanical properties. Thanks to the materials superior weather resistance and UV stability, parts 3D printed with the PolyCore ASA-3012 pellets can be used outdoors, for example in big-scale architecture (bridges, horticulture, landscape) or furniture.
What’s more, this material will perform great in low-to-mid temperature tooling applications.
| Property | Testing Method | Typical Value |
|---|---|---|
| Density (g/cm³ at 21.5 °C) | ASTM D792 (ISO 1183, GB/T 1033) | 1.2 |
| Melt index (g/10 min) | 220 °C, 10 kg | 6 – 10 |
| Glass transition temperature (°C) | DSC, 10 °C/min | 98 |
| Vicat Softening Temperature (°C) | ASTM D1525 (ISO 306 GB/T 1633) | 105 |
| Heat Deflection Temperature (°C) | ISO 75 1.8MPa | 97 |
| Heat Deflection Temperature (°C) | 0.45MPa | 104 |
| Property | Testing Method | Typical Value |
|---|---|---|
| Young’s modulus (MPa) | ASTM D638 (ISO 527, GB/T 1040) | 7237 ± 136 |
| Tensile strength (MPa) | ASTM D638 (ISO 527, GB/T 1040) | 101.3 ± 2.4 |
| Elongation at break (%) | ASTM D638 (ISO 527, GB/T 1040) | 2.6 ± 0.3 |
| Bending modulus (MPa) | ASTM D790 (ISO 178, GB/T 9341) | 7094 ± 89 |
| Bending strength (MPa) | ASTM D790 (ISO 178, GB/T 9341) | 149.6 ± 2.1 |
| Charpy Impact strength (kJ/m²) | ASTM D256 (ISO 179, GB/T 1043) | 8.5 ± 0.5 |
| Property | Testing Method | Typical Value |
|---|---|---|
| Bending modulus (MPa) (X – Y) | Modified ASTM D790 (ISO 178, GB/T 9341) | 3320 ± 160 |
| Bending strength (MPa) (X – Y) | Modified ASTM D790 (ISO 178, GB/T 9341) | 66.6 ± 3.5 |
| Charpy Impact strength (kJ/m²) (X – Y) | Modified ASTM D256 (ISO 179, GB/T 1043) | 5.0 ± 0.32 |
| Bending modulus (MPa) (Z) | Modified ASTM D790 (ISO 178, GB/T 9341) | 1646 ± 170 |
| Bending strength (MPa) (Z) | Modified ASTM D790 (ISO 178, GB/T 9341) | 27.2 ± 2.1 |
| Charpy Impact strength (kJ/m²) (Z) | Modified ASTM D256 (ISO 179, GB/T 1043) | 2.3 ± 0.2 |
| Parameter | Recommended Setting |
|---|---|
| Drying temperature (°C) | 80 |
| Drying Time (h) | 4 |
| Maximum moisture content (%) | 0.1 |
| Barrel – zone 1 temperature (°C) | 200 – 220 |
| Barrel – zone 2 temperature (°C) | 230 – 250 |
| Barrel – zone 3 temperature (°C) | 220 – 240 |
| Nozzle temperature (°C) | 210 – 230 |
| Bed temperature (°C) | Room temperature – 80 |